Fig. 1 | Nano Convergence

Fig. 1

From: Patternable PEDOT nanofilms with grid electrodes for transparent electrochromic devices targeting thermal camouflage

Fig. 1

a Transmittance spectra from 2.5 μm to 25 μm of 150 nm PEDOT film deposited on grid-patterned gold/DSP silicon obtained at every 0.1 V between +0.8 V and −0.8 V versus Ag/AgCl(KClsat) reference electrode. b Cyclic voltammogram of PEDOT films from −1.0 V to 1.0 V (versus Ag/AgCl(KClsat), at a scan rate of 50 mV/s, in a 1.0 M LiClO4-PC electrolyte. c Thickness dependence of transmittance. Neutral (black) and doped (red) state of 150 nm PEDOT film deposited on grid-patterned gold/DSP silicon at the wavelength of 10 μm.(inset) Thickness dependence of transmittance contrast and transmittance contrast ratio. d Thermal images of grid-patterned gold/AR-coated germanium and neutral and doped state of 150 nm PEDOT film on grid-patterned gold/AR-coated germanium