From: Understanding dual precipitation strengthening in ultra-high strength low carbon steel containing nano-sized copper precipitates and carbides
Size (nm)
SANS
vol. fraction
Calculated
σppt (MPa)
TEM
1.7 Cu
10.12
9
9.3986 × 10−3
210.08
TiMo
4.74a
4
7.4509 × 10−3
317.84