From: Deep Q-network to produce polarization-independent perfect solar absorbers: a statistical report
Film #1 mat. | Film #2 mat. | Film #1 height (nm) | Film #2 height (nm) | Cylinder mat. | Cylinder height (nm) | Cylinder diameter (nm) | Lattice spacing (nm) | Abs. AUC (350 – 800 nm) % | Abs. AUC (8 – 13 µm) % |
---|---|---|---|---|---|---|---|---|---|
Ge | GaAs | 1120 | 40 | InAs | 100 | 100 | 50 | 97.61 | 1.37 |
InAs | InP | 1000 | 240 | InAs | 100 | 100 | 50 | 97.32 | 1.50 |
GaAs | InP | 1120 | 40 | InAs | 100 | 100 | 50 | 97.05 | 2.48 |
InAs | GaAs | 1120 | 40 | InAs | 100 | 100 | 50 | 96.75 | 2.56 |
InAs | GaAs | 1110 | 40 | InAs | 100 | 100 | 50 | 96.74 | 2.67 |
GaAs | GaAs | 1120 | 40 | InAs | 100 | 100 | 50 | 96.57 | 2.58 |
InAs | ZnO | 1300 | 290 | TiN | 140 | 100 | 120 | 96.54 | 2.83 |
InAs | InAs | 1000 | 160 | InAs | 100 | 100 | 50 | 96.53 | 2.85 |