From: TEPA impregnation of electrospun carbon nanofibers for enhanced low-level CO2 adsorption
Sample | CO2 adsorption (mmol/g) | |
---|---|---|
0.3% | 100% | |
Physically activated ANF | ||
15-ANF | 0.107 | 1.89 |
15-ANF-TEPA | 0.034 | 0.65 |
30-ANF | 0.151 | 2.10 |
30-ANF-TEPA | 0.119 | 0.97 |
60-ANF | 0.203 | 2.84 |
60-ANF-TEPA | 0.087 | 1.48 |
60-ANF-HNO3 | 0.121 | 1.98 |
60-ANF-HNO3-TEPA | 0.334 | 2.96 |
90-ANF | 0.238 | 2.80 |
90-ANF-TEPA | 0.117 | 1.00 |
Chemically activated ANF | ||
0.01-ANF | 0.021 | 1.96 |
0.01-ANF-TEPA | 0.015 | 0.33 |
0.03-ANF | 0.028 | 2.67 |
0.03-ANF-TEPA | 0.013 | 0.64 |
0.05-ANF | 0.096 | 2.68 |
0.05-ANF-TEPA | 0.020 | 0.41 |