From: Perovskite single-crystal thin films: preparation, surface engineering, and application
Device architecture | Prepared method | Thickness | J SC (mA cm− 2) | V OC (V) | FF (%) | PCE (%) | Year | Refs. |
---|---|---|---|---|---|---|---|---|
FTO/TiO2/MAPbBr3/Au | Cavitation-triggered asymmetrical crystallization method | 1 μm | 6.69 | 1.36 | 69.0 | 6.53 | 2016 | [93] |
ITO/PTAA/MAPbI3/PCBM/C60/BCP/Cu | Space-confined method | 10 μm | 21.0 | 1.08 | 78.60 | 17.80 | 2017 | [49] |
Au/MAPbI3/PCBM/Ag | Space-confined method | 200 nm | 18.33 | 0.80 | 32.90 | 4.83 | 2017 | [54] |
FTO/TiO2/MAPbBr3/Spiro-MeOTAD/Au | Space-confined method | 16 μm | 8.77 | 1.31 | 62 | 7.11 | 2017 | [94] |
FTO/TiO2/MAPbI3/Spiro-OMeTAD/Ag | Space-confined method | ∼3 μm | 22.28 | 0.68 | 59 | 8.78 | 2017 | [91] |
ITO/NiOx/(FAPbI3)0.85(MAPbBr3)0.15/TiO2/Ag | Space-confined method | 24.5 μm | 23.14 | 1.03 | 51 | 12.18 | 2018 | [83] |
ITO/PEDOT:PSS/MAPbI3/PCBM/Ag | Space-confined method | 50 μm | 22.15 | 0.75 | 27 | 4.40 | 2018 | [98] |
ITO/PTAA/MAPbI3/C60/BCP/Cu | Space-confined method | 20 μm | 23.46 | 1.076 | 83.5 | 21.09 | 2019 | [95] |
Au/MAPbI3/C60/BCP/Au | Surface tension-assisted method | 38 μm | 5.06 | 0.66 | 44 | 5.90 | 2019 | [57] |
ITO/PTAA/MAPbI3/C60/BCP/Cu | Low-temperature space-confined method | ∼20 μm | 23.68 | 1.144 | 81 | 21.93 | 2020 | [72] |
ITO/PEDOT:PSS/MAPbI3/PCBM/BCP/Ag | Antisolvent vapor-assisted crystallization method | 300 nm | 22.60 | 1.08 | 82.5 | 20.1 | 2020 | [51] |
PET/ITO/SnO2/MAPb0.5+xSn0.5xI3/Spiro-OMeTAD/ Au/PDMS/Su 8 | Lithography-assisted Epitaxial-growth method | 2 μm | 24.0 | 1.05 | 79.5 | 20.04 | 2020 | [87] |
Au/MAPbI3/C60/BCP/Au | Space-confined method | – | 22.49 | 0.93 | 55.1 | 11.52 | 2020 | [74] |
ITO/PTAA/FA0.6MA0.4PbI3/C60/BCP/Cu | Space-confined method | 15 μm | 26.2 | 1.10 | 79 | 22.80 | 2021 | [96] |
ITO/PTAA:P3HT/MAPbI3/C60/BCP/Cu | Space-confined method | 20 μm | 23.88 | 1.13 | 81.8 | 22.1 | 2022 | [84] |
ITO/PTAA/FA0.55MA0.45PbI3/C60/BCP/Cu | Space-confined method | 20 μm | 22.75 | 1.062 | 76.2 | 18.41 | 2022 | [99] |
ITO/PTAA/MAPbI3(100)/PCBM/C60/BCP/Cu | Space-confined method | 20–25 μm | 23.8 | 1.04 | 78 | 19.3 | 2022 | [79] |
ITO/PTAA/MAPbI3(001)/PCBM/C60/BCP/Cu | Space-confined method | 20–25 μm | 20.1 | 0.98 | 81.4 | 16.0 | 2022 | [79] |
ITO/MeO-2PACz/ FA0.6MA0.4PbI3/PCBM/C60/BCP/Cu | Space-confined method | ∼20 μm | 27.5 | 1.07 | 77 | 23.1 | 2023 | [97] |
ITO/PTAA/MAPbI3/3-mercaptopropyl(dimethoxy)methylsilane (MDMS)/C60/BCP/Cu | Space-confined method | 40 μm | 24.1 | 1.13 | 81.5 | 22.2 | 2023 | [22] |