Table 1 A set of parameters derived from in-plane resistivity \(\rho\)(T), thermopower S(T), and specific heat \(C_\text {p}\)(T) with errors from fitting or calculation for FeSe\(_{1-x}\)S\(_x\)
From: Nanoscale inhomogeneity and the evolution of correlation strength in FeSe\(_{1-x}\)S\(_x\)
x | \(T_\text {s}\) | \(T_\text {c}\) | S/T | \(T_\text {F}\) | \(T_\text {c}/T_\text {F}\) | \(\gamma\) | \(\Theta _\text {D}\) | \(\lambda\) | q | \(m^*\) | \(k_\text {F}\) | \(\nu _\text {F}\) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Â | (K) | (K) | (\(\mu\)V/K\(^2\)) | (\(\times 10^3\) K) | (\(\times 10^{-3}\)) | (mJ/mol K\(^2\)) | (K) | Â | Â | (\(\times m_e\)) | (1/nm) | (km/s) |
0 | 89(1) | 9.3(1) | 0.169(3) | 2.52(5) | 3.69(3) | 9.5(3) | 223(1) | 0.91(2) | 1.72(2) | 6.4(1) | 6.03(3) | 109(1) |
0.03 | 82(1) | 9.9(1) | 0.459(4) | 0.93(1) | 10.6(1) | Â | Â | Â | Â | Â | Â | Â |
0.12 | 65(1) | 10.6(1) | 1.118(5) | 0.38(1) | 27.6(5) | 11.0(2) | 228(1) | 0.97(2) | 9.8(1) | 13.4(1) | 3.39(2) | 29(1) |
0.14 | 61(2) | 10.5(1) | 0.730(6) | 0.58(1) | 18.3(1) | Â | Â | Â | Â | Â | Â | Â |
0.23 | Â | 5.2(1) | 0.201(6) | 2.12(6) | 2.45(2) | 5.2(1) | 226(1) | 0.71(2) | 3.73(4) | 4.6(1) | 4.70(2) | 118(2) |
0.4 | Â | 2.1(1) | -0.05(1) | 8.5(17) | 0.25(4) | 6.7(2) | 212(1) | 0.56(2) | 0.7(1) | 3.5(1) | 8.2(1) | 202(4) |
0.7 | Â | 3.7(1) | 0.017(8) | 25(12) | 0.15(7) | 7.0(1) | 210(1) | 0.65(2) | 0.2(1) | 2.5(1) | 12(2) | 556(70) |
1 | Â | 4.5(1) | 0.018(7) | 24(10) | 0.19(7) | 5.5(1) | 254(1) | 0.65(2) | 0.3(1) | 2.2(1) | 11(1) | 579(26) |